Production and characterization of activated carbon foams with various activation agents for electrochemical double layer capacitors (EDLCs) applications
Yazarlar (4)
Dr. Öğr. Üyesi Zehra Özçifçi Recep Tayyip Erdogan University, Türkiye
Doç. Dr. Mustafa Emirik Recep Tayyip Erdogan University, Türkiye
Prof. Dr. Hakkı Türker Akçay Recep Tayyip Erdogan University, Türkiye
Doç. Dr. Tuğrul YUMAK Sinop Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Colloids and Surfaces A Physicochemical and Engineering Aspects (Q2) | ||
| Dergi ISSN | 0927-7757 Dergi Bilgileri (2024) | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 06-2024 |
| Kabul Tarihi | – | Yayınlanma Tarihi | 01-06-2024 |
| Cilt / Sayı / Sayfa | 690 / 1 / 133851–0 | DOI | 10.1016/j.colsurfa.2024.133851 |
| Makale Linki | http://dx.doi.org/10.1016/j.colsurfa.2024.133851 | ||
| UAK Araştırma Alanları |
Fiziksel Kimya
Enerji
Elektrokimya
|
||
| Özet |
| Sucrose-based activated carbons were obtained by carbon foams with sugar and cobalt (II) nitrate as precursors, followed by using different chemical activation agents. The effect of Co(NO3)2 concentration, the carbonization temperature and the activation agent on the surface chemistry, porosity were investigated. Textural characterization and electrochemical tests were performed on the activated carbon samples (CF). The results showed that the activated carbon produced by H2SO4 and KOH at 800°C had a surface area of 691 m2/g and 1125 m2/g, 89% and 80% of the sample pore structure was microporous, and specific capacitance of 8.4 F/g and 162.2 F/g at a constant current density of 250 mA/g, respectively. K2CO3-activated carbon had 918 m2/g surface area and 63% of the sample pore structure with microporous and 1.4 F/g specific capacitance, H3PO4-activated carbon and ZnCl2-activated … |
| Anahtar Kelimeler |
| Activated carbon | Activation agent | Energy storage | Sucrose | Supercapacitor |
Science Direct
Production and characterization of activated carbon foams with various activation agents for electrochemical double layer capacitors (EDLCs) applications