Analysis of indentation size effect ISE behavior in low load Vickers microhardness testing of Sm123 1 x Nd123 x superconductor system
Yazarlar (7)
Prof. Dr. Şükrü ÇELİK Recep Tayyip Erdogan University, Türkiye
O. Ozturk
Kastamonu University, Türkiye
Kastamonu University, Türkiye
E. Coşkun
Recep Tayyip Erdogan University, Türkiye
Recep Tayyip Erdogan University, Türkiye
M. Sarıhan
Recep Tayyip Erdogan University, Türkiye
Recep Tayyip Erdogan University, Türkiye
E. Asikuzun
Kastamonu University, Türkiye
Kastamonu University, Türkiye
K. Ozturk
Karadeniz Teknical University, Türkiye
Karadeniz Teknical University, Türkiye
C. Terzioglu
Bolu Abant İzzet Baysal Üniversitesi, Türkiye
Bolu Abant İzzet Baysal Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Journal of Materials Science Materials in Electronics (Q1) | ||
| Dergi ISSN | 0957-4522 Dergi Bilgileri (2013) | ||
| Dergi Tarandığı Indeksler | SSCI | ||
| Makale Dili | İngilizce | Basım Tarihi | 07-2013 |
| Cilt / Sayı / Sayfa | 24 / 7 / 2218–2227 | DOI | 10.1007/s10854-013-1082-9 |
| Makale Linki | http://link.springer.com/10.1007/s10854-013-1082-9 | ||
| UAK Araştırma Alanları |
Yoğun Madde Fiziği
|
||
| Özet |
| Indentation size effect (ISE) for (Sm123)1−x(Nd123)x superconducting samples which were fabricated by the solid state reaction technique for values of x = 0.00, 0.05, 0.10, 0.20, and 0.30 was investigated by analyzing the theoretical models. When the experimental data of a number of single crystals which have the different crystal structure and dif... |