Microstructure Evolution during Friction Stir Welding of Mill-Annealed Ti-6Al-4V
Yazarlar (5)
| Makale Türü |
Özgün Makale
(SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
|
||
| Dergi Adı | METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE (Q1) | ||
| Dergi ISSN | 1073-5623 Dergi Bilgileri (2011) | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 03-2011 |
| Cilt / Sayı / Sayfa | 42 / 3 / 745–762 | DOI | 10.1007/s11661-010-0439-4 |
| Makale Linki | https://link.springer.com/article/10.1007/s11661-010-0439-4 | ||
| UAK Araştırma Alanları |
Nükleer Bilimler
|
||
| Özet |
| In this study, mill-annealed Ti-6Al-4V plates were successfully friction stir welded over a wide range of processing parameters using a tungsten-1 pct La2O3 tool. Two K-type thermocouples embedded in the tool indicated that approximately 25 pct of the heat generated during welding was transferred out of the workpiece and into the tool. The thermocouple data, combined with observations of the microstructure, indicated that the stir zone of all welds exceeded the β transus. The microstructure and texture of two representative welds made just above and high above the β transus were investigated with scanning electron microscopy and electron backscatter diffraction (EBSD). The β phase orientations were reconstructed with a fully automated technique from the as-collected α phase data through knowledge of the Burgers orientation relationship. The results suggest that the fine β grains in the stir zone are formed … |